In situ synthesis and characterization of polyaniline-CaCu3Ti4O12 nanocrystal composites

High dielectric constant (ca. 2.4 x 10(6) at 1 kHz) nanocomposite of polyaniline (PANI)/CaCu3Ti4O12 (CCTO) was synthesized using a simple procedure involving in situ polymerization of aniline in dil. HCl. The PANI and the composite were subjected to X-ray diffraction, Fourier transform infrared, thermo gravimetric, scanning electron microscopy and transmission electron microscopy analyses. The presence of the nanocrystallites of CCTO embedded in the nanofibers of PANI matrix was established by TEM. Frequency dependent characteristics of the dielectric constant. dielectric loss and AC conductivity were studied for the PANI and the composites. The dielectric constant increased as the CCTO content increased in PANI but decreased with increasing frequency (100 Hz-1 MHz) of measurement. The dielectric loss was two times less than the value obtained for pure PANI around 100 Hz. The AC conductivity increased slightly up to 2 kHz as the CCTO content increased in the PANI which was attributed to the polarization of the charge carriers.

In situ synthesis of Al2O3-ZrO2-SiCW ceramic matrix composites by carbothermal reduction of natural silicates

In situ formations of Al2O3 + ZrO2 + SiCW ternary composite powders have been obtained by carbothermal reduction of a mixture of Sillimanite. Kaolin and Zircon using two different carbon sources. Products formed were mixtures of alumina and zirconia along with silicon carbide in the form of whiskers. The effects of composition of the reactants, the role of fineness of the starting precursors and the nature of the carbon Source on the final product powder obtained are presented. XRD and SEM analyses indicate complete reaction of the precursors to yield Al2O3 + ZrO2 + SiCW as product powders, with the SiC having whisker morphology. It is also seen that zirconia could be stabilised to some extent in the tetragonal form without any stabilising agent by tailoring the starting materials and their composition. (C) 2002 Published by Elsevier Science B.V.

A Mild Protocol for the Regioselective Ring Opening of Doubly Activated Cyclopropanes by Using Selenolates Generated in Situ: Synthesis of Functionalized Organoselenium Compounds

A variety of functionalized organoselenium compounds were synthesized from doubly activated cyclopropanes and diselenides in the presence of sodium borohydride. A range of substituents were stable under these reaction conditions. Additionally, we extended the scope of the method by reducing nitro groups in the products to give the corresponding selenium-containing unnatural amino acids.

Hydrogelation of bile acid-peptide conjugates and in situ synthesis of silver and gold nanoparticles in the hydrogel matrix

Fabricating supramolecular hydrogels with embedded metal nanostructures is important for the design of novel hybrid nanocomposite materials for diverse applications such as biosensing and chemosensing platforms, catalytic and antibacterial functional materials etc. Supramolecular self-assembly of bile acid-dipeptide conjugates has led to the formation of new supramolecular hydrogels. Gelation of these molecules depends strongly on the hydrophobic character of the bile acids. The possibility of in situ fabrication of Ag and Au NPs in these supramolecular hydrogels by incorporating Ag+ and Au3+ salts was investigated via photoreduction. Chemical reductions of Ag+ and Au3+ salts in the hydrogels were performed without adding any external stabilizing agents. In this report we have shown that the color, size and shape of silver nanoparticles formed by photoreduction depend on the amino acid residue of the side chain.

In Situ Synthesis Of Nanocrystalline Intermetallic Layer During Surface Plastic Deformation Of Zirconium

By means of a surface plastic deformation method a nanocrystalline (NC) intermetallic compound was in situ synthesized on the surface layer of bulk zirconium (Zr). Hardened steel shots (composition: 1.0C, 1.5Cr, base Fe in wt.%) were used to conduct repetitive and multidirectional peening on the surface layer of Zr. The microstructure evolution of the surface layer was investigated by X-ray diffraction and scanning and transmission electron microscopy observations. The NC intermetallic layer of about 25 gm thick was observed and confirmed by concentration profiles of Zr, Fe and Cr, and was found to consist of the Fe100-xCrx compound with an average grain size of 22 nm. The NC surface layer exhibited an extremely high average hardness of 10.2 GPa. The Zr base immediately next to the compound/Zr interface has a grain size of similar to 250 nm, and a hardness of similar to 3.4 GPa. The Fe100-xCrx layer was found to securely adhere to the Zr base. (c) 2007 Elsevier B.V All rights reserved.

In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer During Surface Mechanical Attrition Treatment of Zirconium

The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC) layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 mu m thick and consisted of the intermetallic compound FeCr with an average grain size of 25 +/- 10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa.

In situ synthesis of ZrO2/ZrW2O8 composites with near-zero thermal expansion

In this paper, ZrO2 and WO3 were used as the raw materials to prepare ZrO2/ZrW2O8 composites by in situ reaction method and the thermal expansion property of the composites was studied. This novel method included a heating step up to 1473 K for 24 h, which combines the synthesizing and sintering of ZrW2O8. The result indicates that ZrO2/ZrW2O8 composite shows near-zero thermal expansion when the weight ratio of ZrO2 and WO3 is 2.5:1. Compared with composites prepared previously by non-reactive sintering of ZrO2 and ZrW2O8, the composites show higher relative density and lower porosity.

In-situ synthesis of AlN powders and composite AlN powders with yttrium addition

Using Al-Mg and Al-Mg-Y alloys as raw materials and nitrogen as gas reactants, AIN powders and composite AIN powders by in-situ synthesis method were prepared. AIN lumps prepared by the nitriding of Al-Mg and Al-Mg-Y alloys have porous microstructure, which is favorable for pulverization. They have high purity, containing 1.23 % (mass fraction) oxygen impurity, and consisted of AIN single phase . The average particle size of AIN powders is 6.78 mum. Composite AlN powders consist of AlN phases and rare, earth oxide Y2O3 phase. The distribution of particle size of AIN powders shows two peaks. In view, of packing factor, AIN powders with such size distribution can easily be sintered to high density.

Hyperbranched polymer-assisted hydrothermal in situ synthesis of submicrometer silver tubes

We produced silver tubes with an outer diameter of 1 mu m, wall thickness of 200 nm, and length of hundreds of micrometers by hydrothermal treatment of aqueous solutions of AgNO3 and hyperbranched polyglycidol (HPG) at 165 degrees C. The surfaces of the silver tubes were chemically modified by HPG, which was confirmed by FTIR of the silver tubes.

In situ synthesis of silica gel nanowire/Na+-montmorillonite nanocomposites by the sol-gel route

Silica-gel nanowire/Na+-montmorillonite (Na+-MMT) nanocomposites were prepared by the in situ sol-gel process of tetraethyl orthosilicate (TEOS) in the presence of Na+-MMT and ammonia as catalyst. Microstructure characterization of the nanocomposites was done by SEM, , EDX, XRD and FTIR. It was found that a lot of silica-gel nanowires grew along the edges of Na+-MMT. The combination between the nanowires and Na+-MMT was accomplished via polycondensation of the hydrolyzed TEOS and the edge-OH groups of Na+-MMT.

In situ synthesis of monodisperse luminescent terbium complex-silica nanocomposites

A facile strategy for the in situ synthesis of terbium complex-silica nanocomposites is described. The resultant spherical nanocomposites possess good monodispersity and exhibit luminescent properties of terbium complex.

In situ synthesis and characterization of multiwalled carbon nanotube/Au nanoparticle composite materials

An effective and facile in Situ reduction approach for the fabrication of carbon nanotube-supported Au nanoparticle (CNT/Au NP) composite nanomaterials is demonstrated in this article. Linear polyethyleneimine (PEI) is ingeniously used as both a functionalizing agent for the multiwalled carbon nanotubes (MWNTs) and a reducing agent for the formation of An NPs. This method involves a simple mixing process followed by a mild heating process. This approach does not need the exhaustive surface oxidation process of CNTs. The coverage of Au NPs on CNTs is tunable by varying the experimental parameters, such as the initial molar ratio of PEI to HAuCl4, the relative concentration of PEI and HAUCl(4) to MWNTs, and the temperature and duration of the heat treatment. More importantly, even the heterogeneous CNT/Au composite nanowires are obtainable through this method. TEM, XPS, and XRD are all used to characterize the CNT/Au composite materials. In addition, the optical and electrocatalytic properties are investigated.

In situ synthesis of terbium-benzoic acid complex in sol-gel derived silica by a two-step sol-gel method

Terbium complexes with benzoic acid and its derivatives o-hydroxybenzoic acid and p-hydroxybenzoic acid were in situ synthesized in sol-gel derived silica matrix via a two-step sol-gel process. The formation process of the complex was characterized by fluorescence spectra, absorption spectra and IR spectra. The gels that contain in situ synthesized complexes exhibit the characteristic emission bands of terbium ion. The fluorescence lifetimes of Tb3+ in the silica gels are longer than those in the pure complexes and in the solutions that contain the corresponding complexes. (C) 2000 Elsevier Science Ltd. All rights reserved.

In-situ synthesis of terbium complex with salicylic acid in silica matrix by a two-step sol-gel process

A process for in situ synthesis of terbium complex with salicylic acid by a two-step sol-gel method in silica matrix has been proposed. The luminescence properties of the silica gels codoped with terbium and salicylic acid have also been discussed with respect to that of the gel doped with terbium and that of pure terbium complex with salicylic acid.